1. Product not calendered and powdered

　　原因:工藝配比不合理，膩子中缺少成膜材料

　　Cause: the process ratio is unreasonable, and there is no film-forming material in putty解決方案:增加膩子中膠量(非纖維)比例，

　　Solution: increase the proportion of glue (non fiber) in putty,如聚乙烯醇PVA粉、可再分散粉、其他改性淀粉膠粉、鈉基膨潤土防水膩子粉等。

　　Such as PVA powder, redispersible powder, other modified starch powder, sodium bentonite waterproof putty powder, etc.

　　2 .產品后壓延粉

　　2. Product post calendering powder

　　原因:缺少水硬性膠凝材料或氣硬性膠凝材料，缺少成膜材料解決:增加白水泥或灰鈣粉膠凝材料，膩子要增加膠量(非纖維)的比例。

　　Cause: lack of hydraulic cementitious material or pneumatic cementitious material, lack of film-forming material solution: increase the cementitious material of white cement or lime calcium powder, and increase the proportion of glue (non fiber) of putty.

　　3.該產品當時不掉粉，但經過一段時間后會掉粉原因:缺乏成膜材料膩子,過多的淀粉粘合劑,很長一段時間將在空氣中吸收水分,導致產品粉解決方案:膩子添加膠結材料的比例,如PVA聚乙烯醇粉末,可乳膠粉粉現象主要是產品技術比例不合理;施工技術不合理的理由少;底座太干，吸水較大(快)的底座應先噴水或覆蓋膠水，否則也會滴粉(耐水性膩子質量沒問題)耐水性膩子泛黃問題主要原因:

　　3. The product was not powdered at that time, but it will be powdered after a period of time. The reasons are: the lack of film-forming material putty, too much starch adhesive, which will absorb water in the air for a long time, leading to the product powder solution: the proportion of putty added with cementitious materials, such as PVA polyethylene alcohol powder, the phenomenon of latex powder is mainly due to the unreasonable technical proportion of the product; the reasons for the unreasonable construction technology are few; If the base is too dry, the base with large (fast) water absorption shall be sprayed with water or covered with glue first, otherwise the powder will also be dripped (the quality of water-resistant putty is no problem). The main reasons for the Yellow problem of water-resistant putty are as follows:

　　灰白色的鈣粉過久出現發黃現象

　　Too long yellowing of grey white calcium powder不同地區、不同原料在同一地區的不同礦山，浙江、廣西的一些灰質鈣品種有泛黃現象，河北灰質鈣(鈣輕氧化物)不適合在環境潮濕或基層不完全干燥后進行發黃膩子施工一些基礎添加劑與油灰發生反應耐水膩子操作性差Different areas and different raw materials in different mines in the same area, some varieties of grey calcium in Zhejiang and Guangxi have yellowing phenomenon. Hebei grey calcium (calcium light oxide) is not suitable for yellow putty construction after the environment is humid or the base is not completely dry. Some basic additives react with oil ash, and the operation of water-resistant putty is poor缺乏改善操作性的材料(纖維素、木纖維)

　　Lack of materials to improve operability (cellulose, wood fiber)灰鈣粉等填料的細度不夠，膠凝材料(PVA粉、改性淀粉)過干，吸水量大。

　　The fineness of filler such as lime and calcium powder is not enough, the cementitious material (PVA powder, modified starch) is too dry, and the water absorption capacity is large.

　　耐水膩子的耐水性差

　　Poor water resistance of water resistant putty灰鈣粉、白水泥等填充料比例小，(325目以上通過90%膠凝材料的用量少(PVA粉、改性淀粉)，底料過干，吸水多，導致膩子不能完全粉化。

　　The proportion of lime calcium powder, white cement and other fillers is small, (the amount of 90% cementitious material passing through 325 mesh is small (PVA powder, modified starch), the bottom material is too dry, and the water absorption is too much, so the putty can not be completely powdered.

　　以上是濟南膩子粉廠家為大家介紹的相關內容，想要了解更多內容，歡迎訪問網站：http://www.cnlifelk.cnThe above is the relevant content introduced by Jinan putty powder manufacturer. To learn more, please visit the website: http://www.cnlifelk.cn