The quick drying of putty powder on the wall is mainly influenced by external factors, internal factors and scraping thickness. The external causes are mainly the dryness and humidity of the wall, the weather temperature, humidity, light, etc. The internal causes are mainly the raw material ratio and additive ratio of putty itself. The batch scraping thickness also affects the monotonous speed of putty wall.

　　1.墻體太干：假設墻體太干，會吸收膩子里面的大量水分，膩子粉上墻后會干得很快。這種情況下，先要檢查墻體干濕度，在上膩子前用水噴淋墻體，待無明水前方可施工。

　　1. The wall is too dry: Assuming that the wall is too dry, it will absorb a lot of moisture in the putty, putty powder will dry quickly after the wall. In this case, first check the dryness and humidity of the wall, spray the wall with water before putty, and then construct it before there is no clear water.

　　2.溫度太高：溫度高，光照強，水分蒸發速度加快，膩子上墻后干得也快。特別是在夏季，要避開溫度高、光照強的時段批刮膩子，選擇在早晚溫度低的時間來施工。另外，配料時要把纖維素醚添加量稍微加大一些，增加保水性，減少水分過快蒸發。

　　2. Temperature is too high: high temperature, strong illumination, faster evaporation of water, and faster drying behind putty walls. Especially in summer, we should avoid batch scraping putty in high temperature and strong illumination period, and choose the time of low temperature in the morning and evening to construct. In addition, the dosage of cellulose ether should be slightly increased to increase water retention and reduce excessive evaporation of water.

　　3.膩子質量的問題：有些廠商為了儉省本錢，在膩子配料中用水泥和灰鈣較多。膩子中配用高堿性的水泥，會構成水化太快，招致塑性損失太快，施工時間就縮短；灰鈣吸水量很大，假設添加量大，也會構成膩子上墻時干得快。所以在原料配比時，減少或不用高堿性的水泥，減低灰鈣的用量，假設沒有特殊用途，在普通情況下，普通膩子只需求添加150-200kg灰鈣就夠了。

　　3. Putty quality: Some manufacturers use cement and lime and calcium more in putty ingredients in order to save cost. If alkaline cement is used in putty, it will hydrate too fast, cause plastic loss too fast, and shorten construction time. Grey calcium absorbs a lot of water, assuming a large amount of additions, it will also dry quickly when putty wall is constructed. Therefore, in the proportion of raw materials, reduce or not use high alkaline cement, reduce the amount of lime calcium, assuming no special use, in ordinary cases, ordinary putty only needs to add 150-200 kg lime calcium enough.

　　4.添加劑的問題：在膩子中普通添加多的是纖維素醚，主要是起保水作用。添加纖維素醚，要選擇質量可靠的纖維素醚，質量太差，膩子保水差，批刮困難。纖維素醚的粘度也要適中，粘渡過高，批刮起來過于厚重，費力；粘度太低，保水性不夠，很容易干。普通在灰鈣為200kg的膩子粉中，添加3-4kg粘度為4萬的HPMC。另外可以思索加點木質纖維，價錢低價，可以保水增稠，還可以添加少量的淀粉醚，增加施工性，批刮手感輕不粘刀。

　　4. The problem of additives: cellulose ether is the most commonly added in putty, which mainly plays the role of water retention. When cellulose ether is added, it is necessary to select cellulose ether with reliable quality, which is too poor in quality, poor in water retention of putty and difficult to scrape in batches. The viscosity of cellulose ether should be moderate, too high, too thick and laborious to scrape, too low viscosity, insufficient water retention and easy to dry. Usually, putty powder with 200 kg lime and calcium is added with HPMC with a viscosity of 40,000 yuan (3-4 kg). In addition, we can consider adding some wood fiber, which is cheap, can keep water and thicken, can also add a small amount of starch ether, increase construction, batch scraping feel light non-stick knife.

　　以上內容由濟南膩子粉廠家整理發布，更多相關信息可以點擊我們的官網進行咨詢：http://www.cnlifelk.cn/

　　The above content is organized and published by Jinan putty powder manufacturer. More relevant information can be consulted by clicking on our official website: http://www.cnlifelk.cn./